HICEM LATEX ADHESIVE READY-MIXED MORTAR : POWER-BOND

HICEM Latex Adhesive ready-mixed mortar : Power-Bond

" DIY " with high bonding quality

High standard grade dry-set mortar for high bonding application

Product code : S-03 , SW-03

Price : XXX (Contact distributors) baht / bag

Quantity : 3 kg./bag (10 bag/box)

Using quantity : 0.5-1 square meter/3 kg. (Bag)

Storage : 1 year (from manufacturer date) and keep in good ventilation

HICEM Latex Adhesive ready-mixed mortar is a simple high-grade material used in all types of tile application, especially for repairs. It is one of the most recommended dry-mix that is suitable for even the difficult substrates such as smooth or non-absorbent concrete. It is high recommended for DIY (Do It Yourself) usage. 

fixing-requirement work.

Repairing Application Guidance

  1. Concrete surface must be rigid, clear and free of contaminants that could prevent a good adhesion.
  2. Old, cracked or broken concrete or plaster should be removed to provide a stable base for the HICEM Latex Adhesive ready-mixed mortar.
  3. If the concrete or plaster surface is cracked or uneven, it must be sufficiently smooth to accommodate a mortar application of 5-10 mm.
  4. If the surface to be repaired is not in good condition, it should be pretreated with HICEM Flex Latex Adhesive Emulsion to increase bonding strength.
  5. Prepare HICEM Latex Adhesive ready-mixed mortar into fresh water in proportion of 3:1 (by volume), stirs briskly about 5 mins or until well blended. Let stand for 3-5 mins. Do not add water. Mixture will be viable for approximately 30-40 mins.
  6. Apply mortar to smooth, flat concrete surface.

Open time 20 mins

Setting time 20-30 mins

Water retention 84.70 %

Length change 0.114 %

Slip resistance 0.50 (EN 1308)

Tensile Adhesion Strength 1.0 MPa (N/mm2)

Shear Adhesion Strength 13.36 kgf/cm2 (British Standard 5385 Part 1)

Bond Strength 160.00 kgf/cm2 (ASTM C882-91)

Compressive Strength 340.00 kgf/cm2 (ASTM C109-80)

Flexural Strength 100.70 kgf/cm2 (ASTM C348-86

Transverse deformation 2.50 mm. (EN12002)